Free Newsletter
Register for our Free Newsletters
Newsletter
Zones
Advanced Composites
LeftNav
Aerospace
LeftNav
Amorphous Metal Structures
LeftNav
Analysis and Simulation
LeftNav
Asbestos and Substitutes
LeftNav
Associations, Research Organisations and Universities
LeftNav
Automation Equipment
LeftNav
Automotive
LeftNav
Biomaterials
LeftNav
Building Materials
LeftNav
Bulk Handling and Storage
LeftNav
CFCs and Substitutes
LeftNav
Company
LeftNav
Components
LeftNav
Consultancy
LeftNav
View All
Other Carouselweb publications
Carousel Web
Defense File
New Materials
Pro Health Zone
Pro Manufacturing Zone
Pro Security Zone
Web Lec
Pro Engineering Zone
 
 
 
News

Splat process - interaction of free falling copper droplets with heated substrates

Toyohashi University Of Technology : 23 March, 2011  (New Product)
Researchers have been investigating the processes involved when coatings are applied to materials since the physical mechanisms underlying interactions between surfaces and the coatings sprayed onto them are poorly understood.
Controlling the physical properties of the surfaces of materials, such as metals, is critical for industrial applications ranging non-stick frying pans to the fuselage of aircraft. However, in spite of the wide spread use of the so-called thermal spraying method for coating large areas of materials, there is still insufficient knowledge about the physical mechanisms—in particular the so-called ‘splat process’ whereby thermally sprayed particles change from a distorted shape at the splash stage, to a disk shape—that govern the properties of sprayed particles with substrates. Such an in-depth understanding is important for improving the control and reliability of thermal spray-based coatings.

To clarify these mechanisms, Masahiro Fukumoto and co-workers at the Department of Mechanical Engineering, Toyohashi University of Technology, used millimetre-sized drops of molten copper to analyze exactly what happens in the so-called ‘splat process’ under varying conditions. Since coatings are applied in a range of applications, knowledge of the underlying physical mechanisms will enable industrial processes to be appropriately controlled.

describe their recent findings on the splat formation process to determine why and how disk-shaped splat are formed.

Fukumoto and his group studied the effect of substrate temperature and ambient pressure on the behavior of millimeter sized, molten copper (Cu) droplets free falling onto AISI304 steel substrates.

Important findings included the observation that the porosity at the splat bottom surface dramatically decreased with increasing substrate temperature and decreasing pressure, which implies that substrate wetting by molten droplets during splat flattening may be enhanced by using higher substrate temperatures and lower spray pressures. Notably, good wetting at the splat/substrate interface resulted in disk-shaped splats, and in the opposite case, the formation of splash-splats under poor wetting conditions.

These experiments on the flattening behavior of individual splats will be useful for controlling the properties of coatings on materials by the thermal spraying process.

References

M. Fukumoto, K. Yang, K. Tanaka, T. Usami, T. Yasui, and M. YamadaEffect of Substrate Temperature and Ambient Pressure on Heat Transfer at Interface Between Molten Droplet and Substrate Surface Journal of Thermal Spray Technology 20, 48–57, (2011)Abstract and restricted links: http://www.springerlink.com/content/v81677q1872w52pr/DOI: 10.1007/s11666-010-9537-5Department of Mechanical Engineering, Toyohashi University of Technology, Toyohashi, Aichi 441-8580, JapanRelated information
Advanced Joining Process Laboratory, Toyohashi Tech: http://ajp.pse.tut.ac.jp/